Das, Srashtasrita https://orcid.org/0000-0002-5025-1663 [Institut für Katalyseforschung und -technologie]

Stuckelberger, Michael E. [Deutsches Elektronen-Synchrotron]

Pottbacker, Jan [Pottbacker, Jan]

Jakobtorweihen, Sven [Jakobtorweihen, Sven]

Schroer, Christian G. [Schroer, Christian G.]

Horn, Raimund [Horn, Raimund]

Sheppard, Thomas Lennon [Institut für Technische Chemie und Polymerchemie]
Beitragende:
-
Titel:
Resonant STXM-CT on single wire extracted from Pt/Rh gauzes treated under ammonia oxidation conditions for 24 h
Weitere Titel:
-
Beschreibung:
(Abstract) This tomographic scanning transmission X-ray microscopy (STXM-CT) data was acquired at the P06 microprobe beamline of the PETRA III (Deutsches-Elektronen Synchrotron DESY, Hamburg). The sample measured during this experiment was a single wire extracted from the Pt/Rh gauzes aged under industrial ammonia oxidation conditions for 24 h of time on stream. A detailed description of the dataset can be found in the corresponding readme file and its associated publication.
(Abstract) This tomographic scanning transmission X-ray microscopy (STXM-CT) data was acquired at the P06 microprobe beamline of the PETRA III (Deutsches-Elektronen Synchrotron DESY, Hamburg). The sample measured during this experiment was a single wire extracted from the Pt/Rh gauzes aged under industrial ammonia oxidation conditions for 24 h of time on stream. A detailed description of the dataset can be found in the corresponding readme file and its associated publication.
(Technical Remarks) In this experiment, ex situ STXM-CT was performed on single wires, with angles ranging from 0 to 360 degrees. The single wires were extracted from aged Pt/Rh gauzes treated under industrial ammonia oxidation conditions for 24 h of reaction time. The data available here contains the final and processed tomographic volumes of the wire measured at two energies above and below the Rh K-edge, at 23300 eV and 23208 eV respectively. Each 3D volume has been stacked as slices in each TIFF file provided here.
Schlagworte:
-
Zugehörige Informationen:
-
Sprache:
-
Erstellungsjahr:
Fachgebiet:
Engineering
Objekttyp:
Dataset
Datenquelle:
-
Verwendete Software:
-
Datenverarbeitung:
-
Erscheinungsjahr:
Rechteinhaber/in:

Stuckelberger, Michael E.

Pottbacker, Jan

Jakobtorweihen, Sven

Schroer, Christian G.

Horn, Raimund

Sheppard, Thomas Lennon
Förderung:
-
Name Speichervolumen Metadaten Upload Aktion
Status:
Publiziert
Eingestellt von:
kitopen
Erstellt am:
Archivierungsdatum:
2024-02-22
Archivgröße:
27,0 MB
Archiversteller:
kitopen
Archiv-Prüfsumme:
2907c6e8cd8d78e3fcd5821e7dff4b77 (MD5)
Embargo-Zeitraum:
-